| NOVAPOL® PF-Y821-KPR是一种线性低密度聚乙烯材料,。 该产品在北美洲有供货,加工方式为:薄膜挤出或吹塑薄膜。 NOVAPOL® PF-Y821-KPR的主要特性有: Antiblock 软件 丁烯共聚单体 滑动 加工助剂 抗氧化剂 典型应用领域包括: 包袋/内衬 包装 食品接触应用&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Smoothness,High anti-blocking,Machinable,Food contact compliance,Inoxidizability,Butylene copolymer |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | < 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 38 µ m, blow molded film | 190 | MPa | |
| 1% secant, TD: 38 µ m, blow molded film | 230 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield, 38 µ m, blow molded film | 10.0 | MPa | |
| TD, yield, 38 µ m, blow molded film | 10.0 | MPa | |
| MD, fracture, 38 µ m, blow molded film | 30.0 | MPa | |
| TD, fracture, 38 µ m, blow molded film | 25.0 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 38 µ m, blow molded film | 660 | % | |
| TD, fracture, 38 µ m, blow molded film | 730 | % | |
| Drop hammer impact | |||
| 38 µ m, blow molded film | 140 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 38 µ m, blow molded film | 200 | g | |
| TD: 38 µ m, blow molded film | 390 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 38 µ m, blow molded film | 57 | ASTM D2457 | |
| Haze | |||
| 38 µ m, blow molded film | 11 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| 38.0 µm | 320 | J/cm | Internal Method |
| memo_intro |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |