| About |
|---|
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,High impact resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| yield | 60 | MPa | ISO 527-2 2 |
| Tensile modulus | 2400 | MPa | ISO 527-2 |
| Tensile strain | 6.9 | % | ISO 527-2 |
| Tensile strain | |||
| fracture | 140 | % | ISO 527-2 |
| bending strength | 93 | MPa | ISO 178 |
| Bending modulus | 2300 | MPa | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃ | 0.24 | % | ISO 62 |
| Melt Flow Rate | |||
| 300℃，1.2 kg | 14 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 13 | cm³/10min | ISO 1133 |
| Forming shrinkage rate | |||
| MD,3.2 mm | 0.5-0.7 | % | |
| TD，3.2 mm | 0.5-0.7 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 67 | kJ/m² | ISO 179 |
| Charpy impact strength | |||
| 23℃ | NB | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 124 | ℃ | ISO 75-2 2 |
| 0.45 Mpa, unannealed | 139 | ℃ | ISO 75-2/B |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-05 | 1/℃ | ISO 11359-2 |
| TD | 6.5E-05 | 1/℃ | ISO 11359-2 |
| Ignition point | > 450 | ℃ | |
| Melting temperature | 220 – 230 | ℃ | |
| decomposition temperature | 380 | ℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 23℃ | 6.E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 3.E+14 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 100 Hz | 3.1 | IEC 60250 | |
| 1 Hz | 3.1 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.0090 | IEC 60250 | |
| 100 Hz | 0.0006 | IEC 60250 | |
| Insulation strength | |||
| 2 mmt | 24 | MV/m | IEC 60243-1 |
| Compared to the leakage tracing index | 2 Class | UL 746 A |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Mold shrinkage rate | |||
| 3.2mmt, MD | 0.5 – 0.7 | % | |
| 3.2mmt, TD | 0.5 – 0.7 | % | |
| Drying time | 4 – 8 | hr | |
| Post stage temperature | 260 – 280 | °C | |
| Mid section temperature | 270 – 290 | °C | |
| Front temperature | 270 – 300 | °C | |
| Nozzle temperature | 270 – 300 | °C | |
| Mold temperature | 70 – 100 | °C | |
| Injection pressure | 50 – 150 | MPa | |
| Screw speed | 50 – 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |