| About |
|---|
| 抗紫外线。用于工业配件、汽车部件、电子电器、眼镜行业。中黏度，挤出、注塑成型。 |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，50% RH | – | % | |
| 23 ℃, in water | 0.24 | % | |
| Melt Flow Rate | 7.4 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 7.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5-0.7 | % | ISO 1133 |
| TD：3.2 mm | 0.5-0.7 | % | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ISO 527-1 |
| Yield tensile stress | 61 | MPa | ISO 527-1 |
| Tensile strain | |||
| fracture | 115 | % | ISO 527-1 |
| yield | 5.6 | % | ISO 527-1 |
| Flexural strength | 93 | MPa | ISO 178 |
| Bending modulus | 2300 | MPa | ISO 178 |
| Charpy impact strength with notches | |||
| 23℃ | 76 | kj/m^2 | ISO 179-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 129 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 143 | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-05 | 1/℃ | ISO 11359-2 |
| TD | 6.6E-05 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 100 Hz | 3.1 | IEC 60250 | |
| 1 MHz | 3.1 | IEC 60250 | |
| Dielectric loss factor | |||
| 100HZ | 0.0006 | IEC60250 | |
| 1MHZ | 0.009 | IEC60250 | |
| Volumetric resistance coefficient | 3E+14 | Ω·m | IEC60093 |
| Surface resistance coefficient | 6E+15 | Ω | IEC60093 |
| Dielectric strength | |||
| 1mmt | – | MV/m | IEC60243-1 |
| 2mmt | 24 | MV/m | IEC60243-1 |
| 3mmt | 17 | MV/m | IEC60243-1 |
| Compared to the leakage tracing index | |||
| CTI | 2相当 | UL 746A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | NB | kJ/m² | ISO 179-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |