| About |
|---|
| Novodur® HH-112 is a high heat injection molding grade. It provides extraordinary heat resistance combined with enhanced stiffness. FEATURES Very high heat resistance High stiffness APPLICATIONS Automotive rear lamp housings Glove box caps&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 6.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| MD | 0.55 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2800 | MPa | ASTM D638 |
| Tensile modulus | 2700 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 58.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 58.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Yield, 23 ℃ | 3.1 | % | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 8.0 | % | ISO 527-2 |
| Bending modulus | 2700 | MPa | ASTM D790 |
| Bending modulus | 2700 | MPa | ISO 178 |
| bending strength | 88.3 | MPa | ASTM D790 |
| bending strength | 81.0 | MPa | ISO 178 |
| Ball hardness | 114 | MPa | ISO 2039-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 5.0 | kJ/m² | ISO 179 |
| 23℃ | 12 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 80 | kJ/m² | ISO 179 |
| 23℃ | 140 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 53 | J/m | ASTM D256 |
| 23℃ | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 102 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 110 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 118 | ℃ | ISO 306 |
| B50 | 112 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Maximum operating temperature | 90 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.5 mm | 41 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 30 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |