| Nucrel® 925 is a copolymer of ethylene and methacrylic acid, made with nominally 15 wt% methacrylic acid. It is inherently flexible without the need for plasticizers.The resin can be pigmented, UV-stabilized for exterior applications and painted or plated for special decorative effects. Nucrel® 925 has excellent tensile strength and low temperature impact properties.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Sprayable,Electroplating,low-temperature impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 25 | g/10min | ASTM D1238，ISO 1133 |
| Methacrylic acid content | 15.0 | wt% | |
| Methacrylic Acid Content | 15.0 | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 67.0 | ℃ | ASTM D1525 , ISO 306 |
| Melting peak temperature | 92.0 | ℃ | ASTM D3418 , ISO 3146 |
| freezing point | |||
| — | 74 | ℃ | ASTM D3418 |
| — | 74 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | < 235 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |