NuSil MED-4128

About
NuSil Technology’s restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: LOW TENSION SET, UNCATALYZED&&

About

NuSil Technology’s restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: LOW TENSION SET, UNCATALYZED&&

Product Description
Supplier	NuSil
Generic	硅橡胶
Material Status	Commercial: Active
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
THERMAL	Nominal value	Unit	Test method
Post curing time
200℃	2.0	hr

Supplementary information	Nominal value	Unit	Test method
Cure System	Peroxide

Uncured Properties	Nominal value	Unit
Density	1.11	g/cm³
Curing time
116℃	0.17	hr

Cured Properties	Nominal value	Unit
Shore hardness
Shaw’s A	25
tensile strength	7.14	MPa
200% strain	0.621	MPa
Tensile strain
fracture	800	%
tear strength	12.3	kN/m

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.