Highly resilient, with higher tensile elongation and impact strength than standard grades, NYCAST CP has proven itself in many applications requiring an extra degree of toughness. A copolymer of caprolactam and laurinlactam, NYCAST CP was originally developed specifically for use in ball valve seats in the oil and gas industry. This durable material provides an economical, high-performance bridge between NYCAST 6 and NYCAST 12 formulations. NYCAST CP with its higher elongation, superior dimensional stability and safety yellow color has found itself a superior choice for wobbler box inserts and coupling boxes in the cold rolling steel industry as well as mandrels covers used in paper tube manufacturing plants. High impact resistance High tensile elongation Reduced water absorption Lower hardness Easy to machine&&

About

Highly resilient, with higher tensile elongation and impact strength than standard grades, NYCAST CP has proven itself in many applications requiring an extra degree of toughness. A copolymer of caprolactam and laurinlactam, NYCAST CP was originally developed specifically for use in ball valve seats in the oil and gas industry. This durable material provides an economical, high-performance bridge between NYCAST 6 and NYCAST 12 formulations. NYCAST CP with its higher elongation, superior dimensional stability and safety yellow color has found itself a superior choice for wobbler box inserts and coupling boxes in the cold rolling steel industry as well as mandrels covers used in paper tube manufacturing plants. High impact resistance High tensile elongation Reduced water absorption Lower hardness Easy to machine&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Good flexibility,High impact resistance,Good Dimensional Stability,Elastic,Good Tensile Strength,Copolymer,Durability
Availabilitys	North America
Process Methods	casting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10 to 1.13	g/cm³	ASTM D792
Water absorption rate			ASTM D570
24hr	0.50 to 0.60	%	ASTM D570
saturated	4.0 to 5.0	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	48 to 75	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	204 to 221	℃	ASTM D648
1.8 MPa, unannealed	93.3 to 204	℃	ASTM D648
Continuous use temperature	98.9	℃	ASTM D794
Melting temperature	204 to 216	℃
Linear coefficient of thermal expansion
MD	9.0E-5	1/℃	ASTM D696
Operating temperature
Intermittent	149	℃

Electrical performance	Nominal value	Unit	Test method
Dielectric strength	20 to 24	kV/mm	ASTM D149
Dielectric constant			ASTM D150
60 Hz	3.70		ASTM D150
1 kHz	3.70		ASTM D150
100 kHz	3.70		ASTM D150

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	75 to 81		ASTM D2240
Rockwell hardness
R-level	100 to 115		ASTM D785
Tensile modulus	1650 to 2280	MPa	ASTM D638
tensile strength	60.0 to 79.3	MPa	ASTM D638
Tensile strain
fracture	25 to 80	%	ASTM D638
Bending modulus	1970 to 2650	MPa	ASTM D790
bending strength	103 to 138	MPa	ASTM D790
Compression modulus	1380 to 2070	MPa	ASTM D695
compressive strength	75.8 to 86.2	MPa	ASTM D695
shear strength	52.4 to 62.1	MPa	ASTM D732
friction coefficient
With oneself – dynamic	0.22		ASTM D1894
Load deformation	0.400 to 0.700	%	ASTM D621

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.