| About |
|---|
| NYCOA nanoSEAL™ NS – 8330 UV is a proprietary clay based Nanocomposite made via in-situ polymerization for optimum nano-clay exfoliation. The grade exhibits a higher degree of stiffness and superior toughness compared to standard impact modified Nylons. NYCOA nanoSEAL™ NS – 8330 UV has been specifically formulated for extrusion, blow-molding, and injection molding applications. This grade offers a 55% improvement in barrier properties over traditional Super-Tough Nylons. In addition, this product is UV stabilized for prolonged outdoor exposure to sunlight.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,High impact resistance,Block resin |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| Bending modulus | 2210 | MPa | ASTM D790 |
| bending strength | 75.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 800|无断裂 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 1900|无断裂 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 238 to 249 | °C | |
| Barrel middle temperature | 243 to 260 | °C | |
| Barrel front temperature | 249 to 266 | °C | |
| Nozzle temperature | 249 to 266 | °C | |
| Processing (melt) temperature | 249 to 266 | °C | |
| Mold temperature | 66 to 77 | °C | |
| Screw length to diameter ratio | 16.0:1.0 | ||
| Screw compression ratio | 3.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |