| About |
|---|
| NYCOA 2277 G30I is a 30% glass fiber reinforced, impact modified, Nylon Copolymer resin used for injection molding. This grade features excellent strength and stiffness, dimensional stability, and a lower melting point vs. Nylon 6. NYCOA 2277 G30I is also available in UV stable grades, as well as custom colors. Typical applications include sporting goods, power tool housing, and lawn & garden equipment parts.&& |
| Product Description | |
|---|---|
| Generic | PA Copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,Good Dimensional Stability,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.30 | % | ASTM D955 |
| TD | 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，6.4mm | 130 | J/m | ASTM D256 |
| 23℃，6.4mm | 270 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | ASTM D256 | ||
| -40℃，6.4 mm | 1300 | J/m | ASTM D256 |
| 23℃，6.4 mm | 1300 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 187 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | 116 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 12 | % | ASTM D638 |
| Bending modulus | 6210 | MPa | ASTM D790 |
| bending strength | 145 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |