| NYCOA 436 Nylon is general-purpose low viscosity injection-molding grade Nylon 6 that exhibits excellent melt fluidity, good toughness, stiffness, and strength. NYCOA 436 Nylon is listed by the National Sanitation Foundation under Standard 61 for use in products that come into contact with food or potable water. Typical applications include plumbing fittings, electronics parts, toys, and hardware items such as gears, fittings, casters, bearings, clips, fasteners, plugs, caps, and filter bowls.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good liquidity,Low Viscosity,Quick molding cycle,Food contact compliance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.2 | % | ASTM D955 |
| TD | 1.4 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.7 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 48 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 185 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 68.3 | ℃ | ASTM D648 |
| Melting temperature | 221 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | 86.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2650 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 221 to 241 | °C | |
| Barrel middle temperature | 235 to 252 | °C | |
| Barrel front temperature | 246 to 260 | °C | |
| Nozzle temperature | 254 to 266 | °C | |
| Processing (melt) temperature | 249 to 266 | °C | |
| Mold temperature | 77 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |