| NYCOA 5015 HS is a 15% glass fiber reinforced, heat stabilized Nylon 66 resin used for injection molding. The heat stabilizer system is specially formulated for optimum thermal stability. NYCOA 5015 HS is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. NYCOA 5015 HS is suitable for injection molding and can be found in applications in the hardware, and automotive industries.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Grease resistance,Solvent resistance,Heat Stabilized,Hydrocarbons |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.60 | % | ASTM D955 |
| TD | 0.80 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.90 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 64 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 249 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 232 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| tensile strength | 120 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 6000 | MPa | ASTM D790 |
| bending strength | 174 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 266 to 282 | °C | |
| Barrel middle temperature | 277 to 293 | °C | |
| Barrel front temperature | 288 to 304 | °C | |
| Nozzle temperature | 282 to 302 | °C | |
| Processing (melt) temperature | 288 to 304 | °C | |
| Mold temperature | 77 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |