| About |
|---|
| NYCOA 512 is a fast cycling nucleated and lubricated Nylon 6 used for injection molding applications. This material features outstanding processability, chemical resistance, and an excellent balance of mechanical properties. NYCOA 512 is recognized by Underwriters Laboratories to standard UL 94-V-2 for thickness as low as 0.7 mm. It is also listed by the National Sanitation Foundation (NSF) under standard 61 for use in products that come into contact with food or potable wate Typical applications include plumbing fittings and housings, thin wall molding, toys and hardware items.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Nucleation,Quick molding cycle,Food contact compliance,Lubricating,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.5 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 1.7 | % | ASTM D570 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 90 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 68 | ℃ | ASTM D648 |
| Melting temperature | 221 | ℃ | ATM D789 |
| Vicat Softening Temp |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation strength | |||
| 10.2 | KV/mm | ASTM D149 | |
| Arc resistance | 190 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.71mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| 6.00mm | V-2 | UL 94 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Process temperature | 250 | ℃ |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 46.0 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 120 | R 级 | ASTM D785 |
| ASTM D2583 | |||
| tensile strength | |||
| Yield, 23 ℃ | 86.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | >=40 | % | ASTM D638 |
| bending strength | |||
| Yield, 23 ℃ | 99.0 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2656 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 76.0 | °C | |
| Injection temperature | |||
| Rear barrel temperature | 225 | °C | |
| Central temperature of the barrel | 230 | °C | |
| Barrel front temperature | 250 | °C | |
| Die temperature | 250 | °C | |
| Mold temperature | 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |