| About |
|---|
| NYCOA ASN 27/300 I is a 30% glass fiber reinforced, flame retardant Nylon 6 resin used for injection molding. This resin was specifically formulated to meet the requirement of UL 94 V0 at 1.4mm thickness. NYCOA ASN 27/300 I is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Typical applications include speaker baskets, relay housings, bobbins, and electrical connectors.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Grease resistance,Solvent resistance,Hydrocarbons,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.30 | % | ASTM D955 |
| TD | 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.2 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 140 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 1100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 210 | ℃ | ASTM D648 |
| Melting temperature | 222 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.40 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| Tensile modulus | 9450 | MPa | ASTM D638 |
| tensile strength | 170 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 8220 | MPa | ASTM D790 |
| bending strength | 210 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 232 to 271 | °C | |
| Barrel middle temperature | 243 to 282 | °C | |
| Barrel front temperature | 254 to 291 | °C | |
| Nozzle temperature | 252 to 291 | °C | |
| Processing (melt) temperature | 254 to 291 | °C | |
| Mold temperature | 77 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |