| About |
|---|
| Nylon-MXD6 K7007C is a Polyarylamide (PARA) product. It is available in Asia Pacific, Europe, or North America. Typical application: Food Contact Applications.&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| Equilibrium, 20 ℃, 65% RH | 5.8 | % | ASTM D570 |
| Moisture Regain（20℃） | 3.1 | % | ASTM D570 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Carbon dioxide transfer rate | |||
| 23℃，60% RH | 0.420 | cm³/m²/24 hr | |
| Oxygen permeability | |||
| 23℃ | 0.0700 | cm³/m²/24 hr | |
| 23℃ | 0.110 | cm³/m²/24 hr | |
| Water vapor transmittance | |||
| 40℃，90% RH | 1.4 | g/m²/24 hr |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 20 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 85.0 | ℃ | DSC |
| Melting temperature | 237 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 5.0E-5 | 1/℃ | ASTM D696 |
| Hot deformation temperature | 96 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Half crystallization time | |||
| 160℃ | 1.5 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 108 | ASTM D785 | |
| Tensile modulus | 4700 | MPa | ASTM D638 |
| tensile strength | 99.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.3 | % | ASTM D638 |
| Bending modulus | 4400 | MPa | ASTM D790 |
| bending strength | 160 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Equilibrium, 65% relative humidity |
| 3. 80%RH |
| 4. 60%RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |