| About |
|---|
| The Nymax® 600 Blend Series of nylon 6 materials are “salt-and-pepper” pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials have been formulated to provide improved melt processing, part performance, or surface appearance depending upon grade selected and are offered as an economical alternative to fully compounded products.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Nucleation |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.80 to 1.0 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，3.18 mm | 1.5 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2960 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 85.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 20 | % | ASTM D638 |
| Bending modulus | 2960 | MPa | ASTM D790 |
| bending strength | 124 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 53 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 65.0 | ℃ | ASTM D648 |
| Melting temperature | 220 | ℃ | ASTM D789 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 to 0.20 | % | |
| Barrel rear temperature | 221 to 249 | °C | |
| Barrel middle temperature | 238 to 266 | °C | |
| Barrel front temperature | 243 to 282 | °C | |
| Nozzle temperature | 241 to 279 | °C | |
| Mold temperature | 49 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |