| About |
|---|
| Glass fiber and mineral reinforced PA6 compound with UV resistant&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Heat Stabilized |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 , ISO 1183 |
| Shrinkage rate | 0.30 to 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，3.18 mm | 0.80 | % | ASTM D570 |
| 23℃，24hr | 1.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 7580 | MPa | ASTM D638 |
| — | 7800 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 117 | MPa | ASTM D638 |
| yield | 100 | MPa | ISO 527-2 |
| fracture | 103 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 to 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| — | 7240 | MPa | ASTM D790 |
| — | 7500 | MPa | ISO 178 |
| bending strength | |||
| — | 172 | MPa | ASTM D790 |
| — | 180 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 64 | J/m | ASTM D256-A |
| — | 12 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 190 | ℃ | ISO 75-2/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 to 0.20 | % | |
| Barrel rear temperature | 260 to 277 | °C | |
| Barrel middle temperature | 274 to 288 | °C | |
| Barrel front temperature | 274 to 288 | °C | |
| Nozzle temperature | 274 to 288 | °C | |
| Mold temperature | 49 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |