| About |
|---|
| OLEFISTA™ QM4301D/QMC292 is a Specialty Elastomer material. It is available in Asia Pacific. Important attributes of OLEFISTA™ QM4301D/QMC292 are: Flame Rated Flame Retardant Heat Resistant&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | 特殊弹性体 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | JIS K7112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 92 | JIS K7215 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 19.0 | MPa | JIS K7113 |
| 100% strain | 7.00 | MPa | JIS K7113 |
| Tensile strain | |||
| fracture | 780 | % | JIS K7113 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 180℃，168 hr | 88 | % | JIS K7113 |
| Changes in tensile stress during fracture in air | |||
| 180℃，168 hr | 93 | % | JIS K7113 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -60.0 | ℃ | JIS K6723 |
| Heat Deformation（120℃） | 10 | % | JIS K6723 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 30 ℃ | 9.0E+15 | ohms·cm | JIS K6723 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 25 | % | JIS K7201 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 140 | °C | |
| Barrel 2 zone temperature | 170 | °C | |
| Barrel 3 zone temperature | 180 | °C | |
| Barrel 4 zone temperature | 180 | °C | |
| Connector temperature | 180 | °C | |
| Nozzle temperature | 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |