| About |
|---|
| Cold Temperature Impact Resistant, UV Stabilized, PC/PBT&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,low-temperature impact resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD | 0.50 to 1.1 | % | ASTM D955 |
| MD | 0.50 to 1.1 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 51.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 120 | % | ASTM D638 |
| Bending modulus | 1930 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 640 | J/m | ASTM D256 |
| 23℃，3.2mm | 750 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 96.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, black | HB | UL 94 | |
| 3.00 mm, black | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 116 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 227 to 243 | °C | |
| Barrel middle temperature | 232 to 249 | °C | |
| Barrel front temperature | 238 to 260 | °C | |
| Nozzle temperature | 238 to 260 | °C | |
| Processing (melt) temperature | 238 to 260 | °C | |
| Mold temperature | 49 to 82 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |