OmniLon™ PA6/6 U GR43 BK1000

About
OmniLon™ PA6/6 U GR43 BK1000 is a Polyamide 66 (Nylon 66) product filled with 43% glass fiber. It can be processed by injection molding and is available in North America.&&

Product Description
Generic	PA66
Material Status	Commercial: Active
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 23 ℃	176	MPa	ASTM D638
Tensile strain
fracture	2.0	%	ASTM D638
Bending modulus	12100	MPa	ASTM D790
bending strength
fracture	269	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，3.2mm	96	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	249	℃	ASTM D648
0.45 MPa, unannealed	260	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.12	%
Barrel rear temperature	271 to 293	°C
Barrel middle temperature	271 to 293	°C
Barrel front temperature	271 to 293	°C
Nozzle temperature	271 to 293	°C
Processing (melt) temperature	271 to 293	°C
Mold temperature	27 to 60	°C
Back pressure	0.345	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.