| About |
|---|
| Omnix® FC-4050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture absorption. Omnix® FC-4050 is characterized by high stiffness and strength, very good impact properties, good dimensional stability and high flow properties. This material is an economical alternative for food service applications using die-cast alloys. Omnix® FC-4050 is cleared for use under United States Food and Drug Administration (FDA) Conditions of Use B through H, in contact with all food types except Food Type VI C, Beverages containing more than 8 percent alcohol. Omnix® FC-4050 is also cleared for food contact use by European Union regulations. For specific clearances, please contact your Solvay representative. It processes readily using conventional injection molding machines and methods. Water-cooled molds are suitable for use with this grade. Natural: Omnix® FC-4050 NT 000 Black: Omnix® FC-4050 BK 001&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Quick molding cycle |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | ASTM D792 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 245 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2 |
| Bending modulus | 15000 | MPa | ISO 178 |
| bending strength | 350 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 14 | kJ/m² | ISO 180/A |
| Notched impact strength of cantilever beam | 90 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Barrel rear temperature | 250 | °C | |
| Barrel front temperature | 285 | °C | |
| Processing (melt) temperature | 275 to 290 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. For specific clearances, please contact your Solvay representative. |
| 2. Omnix® FC-4050 is cleared for use under United States Food and Drug Administration (FDA) Conditions of Use B through H, in contact with all food types except Food Type VI C, Beverages containing more than 8 percent alcohol. |
| 3. Typical properties: these are not to be construed as specifications. |
| 4. Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |