| About |
|---|
| Omnix® LF-4060 BK 000 is a 60% Long Glass Fiber reinforced, easy-flowing, heat stabilized HPPA with a very high flexural modulus. It exhibits unique stiffness/toughness combination, an excellent retention of properties in a wide temperature range, as well as outstanding creep and fatigue resistance. Omnix® LF-4060 BK 000 has a pellet length of 9mm and can be processed on most injection-molding machines.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Low CLTE,Low warping,Good flexibility,High impact resistance,Fatigue resistance,Good Tensile Strength,Insulation |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.69 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 22500 | MPa | ISO 527-2 |
| 70℃ | 17000 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 285 | MPa | ISO 527-2 |
| Fracture, 70 ℃ | 200 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 21500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 420 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 45 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 110 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 1.8E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.35 | W/m/K | ISO 22007 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | 35 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Surface resistivity | 1.0E+13 | ohms/sq | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 285 to 300 | °C | |
| Barrel front temperature | 285 to 300 | °C | |
| Nozzle temperature | 285 to 300 | °C | |
| Processing (melt) temperature | < 320 | °C | |
| Mold temperature | 80 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with S.O.P. methods |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |