Omnix® LF-4060 BK 000-9

About
Omnix® LF-4060 BK 000-9 is a 60% Long Glass Fiber reinforced, easy-flowing, heat stabilized HPPA with a very high flexural modulus. It exhibits unique stiffness/toughness combination, an excellent retention of properties in a wide temperature range, as well as outstanding creep and fatigue resistance. Omnix® LF-4060 BK 000-9 has a pellet length of 9mm and can be processed on most injection-molding machines.

About

Omnix® LF-4060 BK 000-9 is a 60% Long Glass Fiber reinforced, easy-flowing, heat stabilized HPPA with a very high flexural modulus. It exhibits unique stiffness/toughness combination, an excellent retention of properties in a wide temperature range, as well as outstanding creep and fatigue resistance. Omnix® LF-4060 BK 000-9 has a pellet length of 9mm and can be processed on most injection-molding machines.

Product Description
Supplier	Solvay
Generic	HPPA
Material Status	Commercial: Active
Features	Good Rigidity,Low CLTE,Low warping,Good flexibility,High impact resistance,Low contractility,Fatigue resistance,Insulation
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.69	g/cm³
Shrinkage rate
TD	0.10	%
Water absorption rate
Equilibrium, 23 ℃, 50% RH	1.2	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	22500	MPa
70℃	17000	MPa
Tensile stress
Fracture, 23 ° C	285	MPa
Fracture, 70 ° C	200	MPa
Tensile strain
fracture	2.0	%
Bending modulus
23℃	21500	MPa
Bending stress (23 ° C)	420	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	45	kJ/m²
Charpy Unnotch Impact strength
23℃	110	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	260	℃
1.8 MPa, unannealed	255	℃
Linear coefficient of thermal expansion
MD	1.8E-5	1/℃
Thermal conductivity coefficient	0.35	W/m/K

Electrical performance	Nominal value	Unit
Dielectric strength
2 mm	35	kV/mm
Compared to the leakage tracing index	600	V
Surface resistivity	1.0E+13	ohms/sq

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80	°C
Drying time	4.0 to 12	hr
Recommended maximum moisture content	0.10	%
Suggested maximum proportion of recycled materials	20	%
Temperature at the rear of the barrel	280 to 300	°C
Temperature in the middle of the barrel	285 to 300	°C
Front temperature of material barrel	285 to 300	°C
Nozzle temperature	285 to 300	°C
Processing (melt) temperature	< 320	°C
Mold temperature	80 to 140	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.