| About |
|---|
| OnFlex™ BIO 5300 series thermoplastic elastomer compounds are soft thermoplastic polyurethane compounds made from renewable natural sources. These compounds contain at least 20% of renewable material as certified according to ASTM-D6866. The OnFlex™ BIO 5300 series compounds are formulated to provide an excellent surface finish, soft-touch haptic, abrasion resistance and mechanical properties.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Negative |
| Features | Renewable resources,Good wear resistance,High scratch resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | DIN 53504 | ||
| TD, 100% strain, 23 ℃, 2 mm | 4.40 | MPa | DIN 53504 |
| MD, 100% strain, 23 ℃, 2 mm | 4.50 | MPa | DIN 53504 |
| TD, 300% strain, 23 ℃, 2.00 mm | 10.0 | MPa | DIN 53504 |
| MD, 300% strain, 23 ℃, 2.00 mm | 10.2 | MPa | DIN 53504 |
| TD, fracture, 23 ℃, 2 mm | 20.0 | MPa | DIN 53504 |
| MD, fracture, 23 ℃, 2.00 mm | 19.8 | MPa | DIN 53504 |
| Tensile strain | DIN 53504 | ||
| TD, fracture, 23 ℃, 2 mm | 520 | % | DIN 53504 |
| Flow rate, fracture, 23 ℃, 2 mm | 500 | % | DIN 53504 |
| tear strength | ISO 34-1 | ||
| TD，23℃，2.00 mm | 64 | kN/m | ISO 34-1 |
| MD，23℃，2.00 mm | 64 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 47 | % | ISO 815 |
| 70℃，22 hr | 71 | % | ISO 815 |
| 100℃，22 hr | 84 | % | ISO 815 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Odor level | 3.2 | VDA 270 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 80 | ISO 868 | |
| Wear amount | 38.0 | mm³ | DIN 53516 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection speed | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1, 7.9 in/min |
| 3. Method A, Trouser |
| 4. Method A3 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |