| About |
|---|
| OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ HT compounds offer excellent mechanical properties, a wide hardness range and good processability.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High Heat Resistance,Ozone resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 3 seconds, 23 ℃, 6.00 mm, injection molding | 70 | DIN 53505 | |
| IRHD hardness | 78 | ISO 48 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | DIN 53504 | ||
| TD, fracture, 23 ℃, 2 mm | 9.40 | MPa | DIN 53504 |
| MD, fracture, 23 ℃, 2.00 mm | 7.50 | MPa | DIN 53504 |
| Tensile strain | DIN 53504 | ||
| TD, fracture, 23 ℃, 2 mm | 800 | % | DIN 53504 |
| Flow rate, fracture, 23 ℃, 2 mm | 630 | % | DIN 53504 |
| tear strength | 37 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| -10℃，22 hr | 43 | % | ISO 815 |
| 23℃，72 hr | 25 | % | ISO 815 |
| 70℃，22 hr | 40 | % | ISO 815 |
| 100℃，22 hr | 51 | % | ISO 815 |
| Stress relaxation | ISO 3384 | ||
| 23℃ | 23 | % | ISO 3384 |
| 23℃ | 15 | % | ISO 3384 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Common material types | 苯乙烯类热塑性弹性体 (TES |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：23℃，2.0 mm | 1.5 to 1.9 | % | Internal Method |
| Apparent viscosity of melt | ASTM D3835 | ||
| 200℃，1340 sec^-1 | 71.2 | Pa·s | ASTM D3835 |
| 200℃，11200 sec^-1 | 18.6 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.9 in/min |
| 3. 168hrs, 25% compression, Method A |
| 4. 100d, 25% compression, Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |