OnForce™ LFT NN-40LCF/001 Grey

About
PolyOne’s Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.&&

About

PolyOne’s Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.&&

Product Description
Supplier	Polyone
Generic	PA66
Material Status	Commercial: Active
Features	Heat Stabilized
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ISO 1183
Shrinkage rate	0.30	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	29000	MPa	ISO 527-2
tensile strength
fracture	305	MPa	ISO 527-2
Tensile strain
fracture	1.5	%	ISO 527-2
Bending modulus	24000	MPa	ISO 178
bending strength	420	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	15	kJ/m²	ISO 179
Charpy Unnotch Impact strength	55	kJ/m²	ISO 179
Drop hammer impact	11.8	J	ASTM D5420

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	250	℃	ISO 75-2/A
8.0 MPa, unannealed	243	℃	ISO 75-2/C

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	290 to 320	°C
Mold temperature	90	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.