| OP – PPO PPOX-30GF是一种聚苯醚 + PS (PPE+PS)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 OP – PPO PPOX-30GF的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 315℃，5.0kg | 2.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.10 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| yield | 103 | MPa | |
| fracture | 103 | MPa | |
| Bending modulus | 6890 | MPa | ASTM D790 |
| bending strength | 131 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 4℃ | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 149 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 143 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 260 to 304 | °C | |
| Barrel middle temperature | 271 to 310 | °C | |
| Barrel front temperature | 282 to 316 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 82.2 to 116 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |