| About |
|---|
| OP – PPS 30GF是一种聚苯硫醚(PPS)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 OP – PPS 30GF的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.30 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| yield | 117 | MPa | |
| fracture | 117 | MPa | |
| Bending modulus | 6890 | MPa | ASTM D790 |
| bending strength | 145 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 4℃ | 37 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 263 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 254 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.20 mm | V-0 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93.3 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 288 to 316 | °C | |
| Barrel middle temperature | 288 to 307 | °C | |
| Barrel front temperature | 288 to 307 | °C | |
| Processing (melt) temperature | 293 to 321 | °C | |
| Mold temperature | 135 to 177 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |