About
OREVAC® 18507 is a chemically functionalized high-density polyethylene with a high content of maleic anhydride. Grafted maleic anhydride induces polarity and leads to outstanding adhesion properties on natural fibers and mineral fillers. Applications OREVAC® 18507 has been designed to be used as coupling agent in halogen free flame retardant cable compounds. It provides outstanding mechanical properties, high tensile strength at break and good elongation, good abrasion and good chemical resistance. OREVAC® 18507 is suitable also to develop a reliable bonding strength between HDPE resins and mineral filler or natural fibers.&&

About

OREVAC® 18507 is a chemically functionalized high-density polyethylene with a high content of maleic anhydride. Grafted maleic anhydride induces polarity and leads to outstanding adhesion properties on natural fibers and mineral fillers. Applications OREVAC® 18507 has been designed to be used as coupling agent in halogen free flame retardant cable compounds. It provides outstanding mechanical properties, high tensile strength at break and good elongation, good abrasion and good chemical resistance. OREVAC® 18507 is suitable also to develop a reliable bonding strength between HDPE resins and mineral filler or natural fibers.&&

Product Description
Supplier	Arkema
Generic	HDPE
Material Status	Commercial: Active
Features	Good bond,Good Tensile Strength,Good wear resistance,Solvent resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.954	g/cm³	ASTM D1505
Density	0.954	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	5.0	g/10min	ISO 1133
190℃，2.16kg	5.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	66		ISO 868
Shaw’s D, molded	66		ASTM D2240
tensile strength
Fracture, molded	10.0	MPa	ASTM D638
Fracture, molded	10.0	MPa	ISO 527-2
Tensile strain
Fracture, molded	800	%	ISO 527-2
Fracture, molded	800	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Melting temperature	128	℃	ISO 11357-3

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.