| About |
|---|
| OREVAC® T 9307 Y is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9307 Y is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates. As a result of high-pressure polymerisation in tubular reactor, OREVAC® T 9307 Y exhibits high transparency (low haze). Applications OREVAC® T 9307 Y is suitable to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils, fiber mats, foams… OREVAC® T 9307 Y can also be used as a skin packaging adhesive on all type of cardboard.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good bond,Terpolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Density | 0.939 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 9.5 to 12 | g/10min | ISO 1133 |
| 190℃，2.16kg | 9.5 to 12 | g/10min | ASTM D1238 |
| Vinyl acetate content | 13.0 to 15.0 | wt% | |
| Maleic anhydride content | 1600 | ppm | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 2.80 mm, molded | 91 | ASTM D2240 | |
| Shore A, 15 seconds, 2.80 mm, molded | 91 | ISO 868 | |
| tensile strength | |||
| Fracture, 2.80 mm, molded | 19.0 | MPa | ISO 527-2/5A/50 |
| Fracture, 2.80 mm, molded | 19.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 2.80 mm, molded | 700 to 900 | % | ISO 527-2/5A/50 |
| Fracture, 2.80 mm, molded | 700 to 900 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 66.0 | ℃ | ASTM D1525 3 |
| Vicat Softening Temp | 66.0 | ℃ | ISO 306/A |
| Melting temperature | 93.0 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 145 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |