| The Orgalloy® LE series is a flexible polyamide alloy. Outstanding properties: processability on PE screw, low moisture absorption, chemical resistance (no known solvents). The grades referenced are higher in rigidity than LE 6000. For profile extrusion, tube extrusion, hollow vessel blow molding and for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good flexibility,Solvent resistance,Low moisture absorption,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，2.16 kg | 3.00 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.8 | % | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 49.0 | MPa | |
| MD, yield | 35.0 | MPa | |
| TD, yield | 35.0 | MPa | |
| MD, fracture | 61.0 | MPa | |
| TD, fracture | 55.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| MD, yield | 16 | % | |
| TD, yield | 16 | % | |
| MD, fracture | 610 | % | |
| TD, fracture | 550 | % | |
| Elmandorf tear strength | |||
| MD | 45 | N | |
| TD | 55 | N |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 23 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 80.0 | ℃ | |
| 1.8 MPa, unannealed | 50.0 | ℃ | |
| Vicat Softening Temp | 128 | ℃ | |
| Melting temperature | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 67 | ||
| Tensile modulus | 2000 | MPa | |
| Nominal tensile fracture strain | > 50 | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |