| Orgalloy® LE 6000是一种聚酰胺6合金（尼龙6合金）产品,。 它可以通过薄膜挤出、吹塑成型、挤出、片材挤出成型、热成型、树脂传递成型、型材挤出成型、压延或注射成型进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 耐冲击 耐热&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Electroplating,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183-2 |
| Melt Volume Rate | |||
| 235℃，2.16 kg | 2.00 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| saturated | 6.4 | % | ISO 62-2 |
| balance | 1.8 | % | ISO 62-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | ISO 527-2 2 |
| tensile strength | |||
| yield | — | MPa | ISO 527-2 2 |
| Tensile strain | |||
| yield | — | % | ISO 527-2 2 |
| Nominal strain at break | — | % | ISO 527-2 2 |
| Tensile Creep Modulus（1 hr） | — | MPa | ISO 899-1 2 |
| Tensile creep modulus | |||
| 1000 hr | — | MPa | ISO 899-1 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 97.0 | ℃ | ISO 306 2 |
| Melting temperature | 220 | ℃ | ISO 11357-3 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| CTI | — | IEC 60112 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 | |
| Flame retardant level | |||
| 3.20 mm | HB | ISO 1210 2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |