| Orgalloy® LT 4060 NAT resin is a very flexible polyamide alloy. Outstanding properties: easy to process, low moisture absorption, good mechanical properties at low temperature. Orgalloy® LT 4060 NAT resin demonstrates a good balance of properties: high flexibility (200 MPa), good thermal performance and ductility at low temperatures.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good flexibility,Ductility,Antifreeze,High Flexibility,Low moisture absorption,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，5 kg | 1.70 | cm³/10min | |
| Shrinkage rate | |||
| TD | 0.90 | % | |
| MD | 0.70 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 600 | MPa | |
| tensile strength | |||
| 50% strain | 20.0 | MPa | |
| Tensile strain | |||
| fracture | > 50 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 80 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 60.0 | ℃ | |
| Vicat Softening Temp | 61.0 | ℃ | |
| Melting temperature | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |