| About |
|---|
| Orgalloy® LT 4060 NAT resin is a very flexible polyamide alloy. Outstanding properties: easy to process, low moisture absorption, good mechanical properties at low temperature. Orgalloy® LT 4060 NAT resin demonstrates a good balance of properties: high flexibility (200 MPa), good thermal performance and ductility at low temperatures.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Electroplating,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183-2 |
| Melt Volume Rate | |||
| 235℃，5 kg | 1.70 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| saturated | 5.0 | % | ISO 62-2 |
| balance | 1.1 | % | ISO 62-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | ISO 527-2 2 |
| tensile strength | |||
| 50% strain | — | MPa | ISO 527-2 2 |
| Tensile strain | |||
| fracture | — | % | ISO 527-2 2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | — | ISO 179/1eA 2 | |
| -30℃ | — | kJ/m² | ISO 179/1eA 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 60.0 | ℃ | ISO 75-2 2 |
| Melting temperature | 217 | ℃ | ISO 11357-3 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| CTI | — | IEC 60112 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 | |
| Flame retardant level | |||
| 3.20 mm | HB | ISO 1210 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |