| Orgalloy® R 60 ES resin is a rigid polyamide 6 alloy. Outstanding properties: easy to process, low moisture absorption, chemical resistance (no known solvents). Blow extrusion grade for technical films: thermal resistance, barrier to gases and aromas, mechanical properties. See LE series for other film grades. |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Retention of aroma ,Low odor,Solvent resistance,Low moisture absorption,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，2.16 kg | 2.00 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 3.3 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | |
| Nominal tensile fracture strain | — | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | — | MPa | |
| MD, yield | 35.0 | MPa | |
| TD, yield | 33.0 | MPa | |
| MD, fracture | 80.0 | MPa | |
| TD, fracture | 60.0 | MPa | |
| Tensile strain | |||
| yield | — | % | |
| MD, yield | 20 | % | |
| TD, yield | 15 | % | |
| MD, fracture | 530 | % | |
| TD, fracture | 530 | % | |
| Elmandorf tear strength | |||
| MD | 40 | N | |
| TD | 35 | N | |
| Oxygen transfer rate | |||
| 0% RH：23℃ | 170 | cm³/m²/bar/24 hr | |
| 85% RH：23℃ | 170 | cm³/m²/bar/24 hr |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | — | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | |
| 1.8 MPa, unannealed | 75.0 | ℃ | |
| Vicat Softening Temp | 134 | ℃ | |
| Melting temperature | 220 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 9.3E-5 | 1/℃ | |
| TD | 1.3E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | — | ohms·cm | |
| Dielectric strength | 38 | kV/mm | |
| Relative permittivity | |||
| 100 Hz | — | ||
| 1 MHz | — | ||
| Dissipation factor | |||
| 100 Hz | — | ||
| 1 MHz | — | ||
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |