| About |
|---|
| Orgalloy® RS 66 series is a rigid polyamide 66 alloy. Outstanding properties: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties. The grades referenced: 20% glass filled, for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA66 Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good Dimensional Stability,Solvent resistance,Low moisture absorption,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，2.16 kg | 13.0 | cm³/10min | |
| Shrinkage rate | |||
| TD | 0.60 | % | |
| MD | 0.40 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 2.3 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 240 | ℃ | |
| 1.8 MPa, unannealed | 220 | ℃ | |
| Vicat Softening Temp | 195 | ℃ | |
| Melting temperature | 255 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | — | ohms·cm | |
| Dielectric strength | 35 | kV/mm | |
| Relative permittivity | |||
| Dissipation factor | |||
| 100 Hz | — | ||
| 1 MHz | — | ||
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 78 | ||
| Tensile modulus | 6320 | MPa | |
| tensile strength | |||
| fracture | 115 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |