| About |
|---|
| OXPEKK® IG200 is a Polyetherketoneketone (PEKK) material. It is available in Europe or North America for injection molding. Primary attribute of OXPEKK® IG200: Crystalline. Typical application of OXPEKK® IG200: Medical/Healthcare&& |
| Product Description | |
|---|---|
| Generic | PEKK |
| Material Status | Commercial: Active |
| Features | Crystal |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，8.40kg | 100 to 120 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.4 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | < 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4410 | MPa | ASTM D638 |
| Bending modulus | 4550 | MPa | ASTM D790 |
| compressive strength | 207 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 175 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.1E-5 | 1/℃ | ASTM D696 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |