| About |
|---|
| Excellent performance at high temperatures High heat deflection temperature High strength and excellent shape stability Very good impact resistance Processing by state-of-the art sinter technologies Powder or granules are commercially available Small particle size Low wear and friction behaviour&& |
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | TPI |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Low coefficient of friction,Machinable,High Heat Resistance,Good wear resistance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 3580 | MPa | ISO 527-2 |
| tensile strength | 140 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 10 | % | ISO 527-2 |
| Compression modulus | 1960 | MPa | ISO 604 |
| compressive strength | 470 | MPa | ISO 604 |
| Compressive strain | |||
| destroy | 58 | % | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 343 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 319 | ℃ | ISO 75-2/Af |
| Glass transition temperature | 337 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. AC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |