| Product Description | |
|---|---|
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ultra high toughness,Solvent resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.03 | g/cm³ | GB/T1033-1986 |
| Water absorption rate | |||
| 24 hrs | 0.2-0.3 | % | GB/1034-1998 |
| Shrinkage rate | 0.3-0.4 | % | GB/T15585-199 5 |
| Melt Flow Rate | |||
| 250℃/2.16kg | 8 | g/10min | GB/T3682-2000 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shaw hardness | |||
| D-level | 79 | GB/T2411-1980 | |
| tensile strength | |||
| 50mm/min | 61 | MPa | GB/T1040-1992 |
| Tensile strain | |||
| 50mm/min | 220 | % | GB/T1040-1990 |
| bending strength | |||
| 10mm/min | 70 | MPa | GB/T9341-2000 |
| Bending modulus | |||
| 10mm/min | 1248 | MPa | GB/T9341-2000 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 190-200 | ℃ | GB/T4608-1984 |
| Hot deformation temperature | |||
| 0.45Mpa | 113 | ℃ | GB/T1634-2004 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | GB/T1043-1993 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL-94 | |
| 3.0 mm | HB | UL-94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 38 | KV/mm | IEC60243-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |