| About |
|---|
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Burn residue | 33 | % | |
| Density | 1.37 | g/cm³ | ISO 1183-A |
| Water absorption rate | |||
| 23℃，24hr | 0.1 | % | ISO 62 |
| Shrinkage rate | |||
| MD | – | % | |
| TD | – | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 108 | R 级 | |
| tensile strength | 167 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 3.6 | % | ISO 527 |
| bending strength | 230 | MPa | ISO 527 |
| Bending modulus | 8200 | MPa | ISO 178 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | – | Ohm | IEC 60093 |
| Dielectric strength | – | KV/mm | IEC 60243 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 200 | ℃ | ISO 75-2 |
| melting point | 195 | ℃ | ISO 3146C |
| Scorching hot wire | |||
| 1.6mm | 650 | ℃ | IEC 695-2-1 |
| Flame retardant level | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | – | kJ/m² | ISO 179-LeA |
| Charpy Notched Impact Strength | |||
| 23℃ | 18 | kJ/m² | ISO 179-LeA |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Ejection temperature | 230-280 | ℃ | |
| Mold temperature | 70-120 | ℃ | |
| Plastic drying temperature | 100-130 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |