| About |
|---|
| 玻纤增强尼龙66， 良好的尺寸稳定性，高耐热性,高强度,高刚度 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 1 mm/min | 21000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 5 mm/min | 2.0 | % | ISO 527-2 |
| 5 mm/min | 250 | MPa | ISO 527-2 |
| bending strength | |||
| 2 mm/min | 390 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 19000 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 122 | N/mm² | ISO 2039-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 260 | ℃ | ISO 75-2 |
| 1.8 MPa | 250 | ℃ | ISO 75-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10^15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm in oil | kV/mm | IEC 60243-1 |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.9 | % | ISO 62 |
| Ash Content | 60 | % | ISO 3451/1 |
| Flame retardant level | |||
| 1.60 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | |||
| MD | 0.2 | % | ISO 2577 |
| TD | 0.5 | % | ISO 2577 |
| Density | 1.72 | g/cm³ | ISO 1183-1 |
| Process Conditions | |||
|---|---|---|---|
| Typical processing conditions | Nominal value | Unit | Test method |
| Melt temperature | 270~305 | °C | |
| Temperature of the rear section of the barrel | 270~285 | °C | |
| Temperature in the middle section of the barrel | 280~300 | °C | |
| Temperature of the front section of the material barrel | 290~305 | °C | |
| Mold temperature | 40-120 | °C | |
| Upper limit of processing temperature | 320 | °C | |
| Injection molding speed | 中速to高速 | ||
| Pre-drying | 100~130°C, 4~6hr | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |