| About |
|---|
| All Politem Plastik Polyamide Resins are recycled from Post Industrial Fiber Waste Streams&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 to 1.14 | g/cm³ | ISO 1183 |
| Ash Content | 0.30 to 0.50 | % | ISO 3451-4 |
| humidity | 0.10 to 0.30 | % | ISO 15512/B |
| Relative viscosity | 2.60 to 2.80 | ||
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 to 7.0 | kJ/m² | ISO 179-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 220 to 225 | ℃ | ISO 3146 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| DSC Analysis | > 96 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 to 85 | ISO 868 | |
| Tensile modulus | 3000 to 4000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 80.0 to 90.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 5.0 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Formic |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |