| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Hardness |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，5 kg | 11.0 | cm³/10min | ISO 1133 |
| 300℃，1.2 kg | cm³/10min | ||
| Heat resistance | |||
| HDT,1.8MPa | 100 | ℃ | |
| Impact resistance | |||
| 15 | kJ/m² | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 56.0 | MPa | ISO 527-2\ISO 527-1 |
| Yield, 23 ℃ | 68.0 | MPa | ISO 527-2\ISO 527-1 |
| Tensile strain | |||
| fracture | 93 | % | ISO 527-2\ISO 527-1 |
| Bending modulus | 2580 | MPa | ISO 178 |
| bending strength | 95 | MPa | ISO 178 |
| surface hardness | |||
| Pencil hardness | F | ASTM D3363 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 6 | kJ/m² | ISO 179 |
| 23℃ | 15 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-1/2 |
| 0.45 MPa, unannealed | 118 | ℃ | ISO 75-1/2 |
| Process Conditions | |||
|---|---|---|---|
| Forming conditions | Nominal value | Unit | Test method |
| Preparation drying temperature | 110 | ℃ | |
| Preparation drying time | 4~8 | hr | |
| Forming temperature | 250~280 | ℃ | |
| Setting temperature | 50~80 | ℃ | |
| Injection Pressure | 60~150 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |