| About |
|---|
| Carbon fiber reinforced grades-20% Carbon fiber, Flame resistant grade, Non-bromine/non phosphor type&& |
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Halogen free,Good flexibility,V-2,Good Rigidity |
| Availabilitys | North America,Asia Pacific,Latin America,Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding shrinkage | Internal Method | ||
| TD：4.0 mm | 0.30 to 0.50 | % | Internal Method |
| MD：4.0 mm | 0.020 to 0.20 | % | Internal Method |
| Water Absorption | |||
| 23℃，24hr | 0.14 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 13600 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| Broken BRK | 125 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Broken BRK | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| Flexural Strength | 185 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 28 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 147 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 149 | ℃ | ISO 75-2/B |
| Vicat Softening Temperature | |||
| B50 | 152 | ℃ | ISO 306 |
| Coeff. of linear thermal expansion | |||
| TD | 6.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Electrical performance Elec, 1.50 mm | 80.0 | ℃ | UL 746 |
| Strength mechanical performance str, 1.50 mm | 80.0 | ℃ | UL 746 |
| Impact mechanical performance Imp, 1.50 mm | 80.0 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 1.0E+2 | ohms | IEC 60093 |
| Volume Resistance | 10 to 1.0E+3 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-2 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |