| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 17 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 61 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | >50 | ISO 527-2 | |
| bending strength | 94 | MPa | ISO 178 |
| bending strength | 2400 | MPa | ISO 178 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3000 µm | 88.0 | % | ISO 13468-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 127 | ℃ | ISO 75-2/Af |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 69 | kJ/m² | ISO 179-1eA |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 100-130 | °C | |
| Drying time | 2.0-6.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 250-290 | °C | |
| Barrel middle temperature | 260-300 | °C | |
| Barrel front temperature | 270-310 | °C | |
| Mold temperature | 60-140 | °C | |
| Nozzle temperature | 280-320 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |