| PC alloy grade&& |
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-1,5VB,V-0,5VA,HB |
| Availabilitys | Africa & Middle East ,North America,Europe,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 21.0 | cm³/10min | ISO 1133 |
| Molding shrinkage | Internal Method | ||
| TD：4.0 mm | 0.50 to 0.70 | % | Internal Method |
| MD：4.0 mm | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| 23℃，24hr | 0.22 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| Broken BRK | 60.0 | MPa | ISO 527-2/50 |
| Yield yld | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Broken BRK | 100 | % | ISO 527-2/50 |
| Yield yld | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Strength | 95.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 60 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 113 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 126 | ℃ | ISO 75-2/B |
| Coeff. of linear thermal expansion | |||
| TD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Electrical performance, 1.50 mm | 95.0 | ℃ | UL 746 |
| Strength mechanical performance, 1.50 mm | 95.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.50 mm | 95.0 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | UL 94 | ||
| 0.45 mm | HB | UL 94 | |
| 1.00 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index GWFI | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 930 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 930 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | IEC 60695-2-13 | ||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 825 | ℃ | IEC 60695-2-13 |
| 2 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 825 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |