| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| Electrical performance | Nominal value | Unit | Test method |
| Tensile fracture stress | 65 | MPa | ASTM D638 |
| Tensile fracture with specified deformation | 115 | % | ASTM D638 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 2000 | MPa | ASTM D790 |
| bending strength | 76 | MPa | ASTM D790 |
| tensile strength | |||
| yield | 55 | MPa | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃，6.4mm | 700 | J/m | ASTM D256 |
| -30℃，6.4mm | 520 | J/m | ASTM D256 |
| 23℃，3.2mm | 780 | J/m | ASTM D256 |
| -30℃，3.2mm | 680 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 128 | ℃ | ISO 75-1/2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | |||
| TD：4.0 mm | 0.5~0.7 | % | Internal Method |
| MD：4.0 mm | 0.5~0.7 | % | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel temperature | 270～320 | ℃ | |
| Mold temperature | 80～120 | ℃ | |
| Screw speed | 40～100 | rpm | |
| Injection pressure | 98.1～147.1 | MPa | |
| Back pressure | 10 | MPa or less | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |