Panlite®L-1225LL

About
Panlite®L-1225LL（QF00635LL）该牌号为红外穿透PC。Panlite ® ® 光传感器用等级、除了拥有 Panlite ® ® 的耐冲击性、耐热性、尺寸稳定性以外，还具有能够吸收波长约 700nm 以下的光线，并且能够透过 700nm 以上近红外光的性质。基于这个特性，该材料可应用于光传感器的外壳部品。 Panlite ® ® 光传感器用等级的特征 Ⅰ ．在近红外光领域具有优异的光透过性。 Ⅱ ．高耐热性，优异的热安定性。 Ⅲ ．优异的脱模性、流动性

About

Panlite®L-1225LL（QF00635LL）该牌号为红外穿透PC。Panlite ® ® 光传感器用等级、除了拥有 Panlite ® ® 的耐冲击性、耐热性、尺寸稳定性以外，还具有能够吸收波长约 700nm 以下的光线，并且能够透过 700nm 以上近红外光的性质。基于这个特性，该材料可应用于光传感器的外壳部品。
Panlite ® ® 光传感器用等级的特征
Ⅰ ．在近红外光领域具有优异的光透过性。
Ⅱ ．高耐热性，优异的热安定性。
Ⅲ ．优异的脱模性、流动性

Product Description
Supplier	TEIJIN
Generic	Polycarbonate
Material Status	Commercial: Active
Features	High infrared light transmittance

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Volume Rate
300℃，1.2 kg	54	cm³/10min	ISO 1133
Density	1.2	g/cm³	ISO 1183
Water absorption rate
23℃，24hr	0.2	%	ISO 62
Shrinkage rate
MD	0.5 ～ 0.7	％	Internal Method
TD	0.5 ～ 0.7	％	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2450		ISO 527-1-2
tensile strength
yield	63	MPa	ISO 527-1-2
Tensile strain
yield	6	％	ISO 527-1-2
fracture	>50	％	ISO 527-1-2
Bending modulus	2400	MPa	ISO 178
	96	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa	124	℃	ISO 75-1/2
0.45 MPa	138	℃	ISO 75-1/2
Linear coefficient of thermal expansion
MD	7E-5	/℃	ISO 11359-2
TD	7E-5	/℃	ISO 11359-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength		kJ/m²
23℃	NB		ISO 179
23℃	38		ISO 179
30°C	9		ISO 179

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.