PAXOTHENE® NA205-15

About
PAXOTHENE NA205-15 (LDPE) is specially developed for extrusion coating on various substrates such as paper, cellophane, aluminum foil, polyolefin film, polyester film and nylon film. NA205-15 also possesses excellent adhesion to a variety of porous substrates such as paper as well as non-porous substrates such as cellophane and foil. Low moisture-vapor transmission rates in combination with excellent heat sealability makes NA205-15 a good coating material. Concerning processability, good flow characteristics and low neck-in of NA205-15 provide high line speed and reduce the loss of resin in the extrusion coating.&&

About

PAXOTHENE NA205-15 (LDPE) is specially developed for extrusion coating on various substrates such as paper, cellophane, aluminum foil, polyolefin film, polyester film and nylon film. NA205-15 also possesses excellent adhesion to a variety of porous substrates such as paper as well as non-porous substrates such as cellophane and foil. Low moisture-vapor transmission rates in combination with excellent heat sealability makes NA205-15 a good coating material. Concerning processability, good flow characteristics and low neck-in of NA205-15 provide high line speed and reduce the loss of resin in the extrusion coating.&&

Product Description
Supplier	USI
Generic	LDPE
Material Status	Commercial: Active
Features	Good heat sealing,Good liquidity,Low shrinkage,Food contact compliance,Good bond,Low density
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.919	g/cm³	ASTM D1505
Melt Flow Rate	3.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	53		ASTM D2240

film	Nominal value	Unit	Test method
tensile strength			ASTM D882
MD, yield	9.02	MPa	ASTM D882
TD, yield	9.02	MPa	ASTM D882
MD, fracture	19.1	MPa	ASTM D882
TD, fracture	15.4	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	330	%	ASTM D882
TD, fracture	540	%	ASTM D882
Drop hammer impact	98	g	ASTM D1709

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -76.0	℃	ASTM D746
Vicat Softening Temp	100	℃	ASTM D1525
Melting peak temperature	109	℃	ASTM D3418

optical performance	Nominal value	Unit	Test method
gloss
60°	100		ASTM D523
Haze	6.0	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.