| About |
|---|
| UL94 3.0mmV-0 15%玻纤增强，经济型规格载体。线圈骨架、插件、开关、插座、继电 器、车灯底座、连接器、OA风扇叶片、骨架、灯具外壳、热熔胶枪外壳、FBT增湿器等需要高强度，高电器条件，抗温的注塑成品用。 |
| Product Description | |
|---|---|
| Supplier | Nan Ya |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Food contact compliance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| 3.0 mm | 0.2~1.2 | % | ASTM D755 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 130 | MPa | ASTM D638 |
| Bending modulus | 8000 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notch impact strength | 76.8 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 206 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation failure strength (3.2mm) | 20 | Kv/mm | ASTM D149 |
| Arc resistance | 80 | sec | ASTM D495 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Nozzle temperature | 245 | ℃ | |
| Barrel temperature – front section | 240 | ℃ | |
| Barrel temperature – middle section | 240 | ℃ | |
| Barrel temperature – rear section | 235 | ℃ | |
| Mold temperature | 80 | ℃ | |
| Injection pressure | 30~40 | MPa | |
| Screw speed | 80 | rpm | |
| Injection speed | 最大 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |