| About |
|---|
| Product Description | |
|---|---|
| Supplier | lutianhua-group |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.5-0.7 | % | ISO 94 |
| Melt Flow Rate | |||
| 260℃，5kg | 12 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50 mm/min | 50 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 50 mm/min | ＞30 | % | ISO 527 |
| Tensile modulus | |||
| 50 mm/min | 2200 | MPa | ISO 527 |
| bending strength | |||
| 2 mm/min | 70 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 50 | kJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8MPa | 90 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1E14 | ohms | IEC 60093 |
| Volume resistivity | 1E16 | ohms·cm | IEC 60093 |
| Relative permittivity | 3.0 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Feed temperature | 220-240 | ℃ | |
| Intermediate section temperature | 230-250 | ℃ | |
| Front temperature | 240-260 | ℃ | |
| Nozzle temperature | 250-265 | ℃ | |
| Mold temperature | 50-80 | ℃ | |
| Injection pressure | 中低压 | ||
| Injection speed | 中低速 | ||
| Maintaining pressure | 50-70 | % | |
| Melt back pressure | 50-100 | Bar | |
| drying temperature | 80-100 | ℃ | |
| Drying time | 4-6 | h | |
| Maximum moisture content | 0.02 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |